LNP™ LUBRICOMP™ LL003 compound
聚醚醚酮
SABIC Innovative Plastics
产品说明:
LNP LUBRICOMP LL003 is a compond based on Polyetheretherketone resin containing 15% PTFE Lubricant. Added feature of this material is: Wear Resistant.
Also known as: LNP* LUBRICOMP* Compound LL-4030
Product reorder name: LL003
|
添加剂 |
· PTFE润滑剂 (15%) |
|||
|
特性 |
|
|||
|
加工方法 |
· 注射成型 |
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
|
|
ASTM D792 |
|
-- |
1.39 |
|
|
|
-- |
1.39 |
g/cm³ |
|
|
收缩率 |
|
|
ASTM D955 |
|
流动 : 24小时 |
9.0E-3 到 0.020 |
in/in |
|
|
横向流动 : 24小时 |
0.010 到 0.030 |
in/in |
|
|
吸水率 |
|
|
|
|
24 hr, 50% RH |
0.078 |
% |
ASTM D570 |
|
平衡, 73°F, 50% RH |
0.089 |
% |
ISO 62 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
-- 2 |
436000 |
psi |
ASTM D638 |
|
-- |
446000 |
psi |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
屈服 3 |
9340 |
psi |
ASTM D638 |
|
屈服 |
8990 |
psi |
ISO 527-2/5 |
|
断裂 3 |
9340 |
psi |
ASTM D638 |
|
断裂 |
8990 |
psi |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
屈服 3 |
4.6 |
% |
ASTM D638 |
|
屈服 |
3.3 |
% |
ISO 527-2/5 |
|
断裂 3 |
4.6 |
% |
ASTM D638 |
|
断裂 |
|
|
|
- BIS00YZ BIS U-626-069-111-06-ST31
- BIS00YY BIS U-626-069-111-06-ST32
- BIS01FY BIS U-830-4-011-H-0
- BIS01FZ BIS U-830-4-011-H-1
- BIS00T3 BIS V-6102-019-C001
- BIS012E BIS V-6102-019-C101
- BIS012F BIS V-6106-034-C002
- BIS0122 BIS V-6106-034-C004
- BIS01H5 BIS V-6106-034-C008
- BIS014C BIS V-6106-034-C102
- BIS0146 BIS V-6106-034-C104
- BIS01H6 BIS V-6106-034-C108
- BIS0186 BIS V-6107-039-C005
- BIS01EF BIS V-6107-039-C005-SA1
- BIS018J BIS V-6107-039-C006