LNP™ LUBRICOMP™ LCL33EXQ compound
聚醚醚酮
15% 碳纤维增强材料
SABIC Innovative Plastics
产品说明:
LNP LUBRICOMP LCL33EXQ is a compound based on Polyetheretherketone containing 15% Carbon Fiber, 15% PTFE. Added features of this material include: Wear Resistant, Easy Molding.
Also known as: LNP* LUBRICOMP* Compound LCL33EXQ
Product reorder name: LCL33EXQ
|
填料/增强材料 |
· 碳纤维增强材料, 15% 填料按重量 |
|||
|
添加剂 |
· PTFE润滑剂 (15%) |
|||
|
特性 |
|
|||
|
加工方法 |
· 注射成型 |
|
物理性能 |
额定值 |
单位制 |
测试方法 |
|
比重 |
1.45 |
|
ASTM D792 |
|
溶化体积流率（MVR） (300°C/5.0 kg) |
1.83 |
in³/10min |
ASTM D1238 |
|
机械性能 |
额定值 |
单位制 |
测试方法 |
|
拉伸模量 |
|
|
|
|
-- 2 |
2.32E+6 |
psi |
ASTM D638 |
|
-- |
2.03E+6 |
psi |
ISO 527-2/1 |
|
抗张强度 |
|
|
|
|
断裂 3 |
26800 |
psi |
ASTM D638 |
|
断裂 |
26300 |
psi |
ISO 527-2/5 |
|
伸长率 |
|
|
|
|
断裂 3 |
1.8 |
% |
ASTM D638 |
|
断裂 |
1.6 |
% |
ISO 527-2/5 |
|
弯曲模量 |
|
|
|
|
1.97 in 跨距 4 |
1.94E+6 |
psi |
ASTM D790 |
|
-- 5 |
1.96E+6 |
psi |
ISO 178 |
|
弯曲应力 |
|
|
|
|
-- |
40000 |
psi |
ISO 178 |
|
断裂, 1.97 in 跨距 4 |
40200 |
psi |
ASTM D790 |
|
泊松比 |
0.43 |
|
ISO 527-2 |
|
摩擦系数 |
|
|
ASTM D3702 Modified |
|
Dynamic |
0.37 |
|
|
|
Static |
0.35 |
|
|
|
磨损因数 - Washer |
14.0 |
10^-10 in^5-min/ft-lb-hr |
ASTM D3702 Modified |
|
冲击性能 |
额定值 |
单位制 |
测试方法 |
|
悬壁梁缺口冲击强度 |
|
|
|
|
73°F |
1.3 |
ft·lb/in |
ASTM D256 |
|
73°F 6 |
|
|
|
- BIS00YZ BIS U-626-069-111-06-ST31
- BIS00YY BIS U-626-069-111-06-ST32
- BIS01FY BIS U-830-4-011-H-0
- BIS01FZ BIS U-830-4-011-H-1
- BIS00T3 BIS V-6102-019-C001
- BIS012E BIS V-6102-019-C101
- BIS012F BIS V-6106-034-C002
- BIS0122 BIS V-6106-034-C004
- BIS01H5 BIS V-6106-034-C008
- BIS014C BIS V-6106-034-C102
- BIS0146 BIS V-6106-034-C104
- BIS01H6 BIS V-6106-034-C108
- BIS0186 BIS V-6107-039-C005
- BIS01EF BIS V-6107-039-C005-SA1
- BIS018J BIS V-6107-039-C006