13/04

E410NiMo-15

E 13 4 B 22

0.04

0.5

<0.4

12.0

4.5

0.5

14K

≈E410-15

E 13 1 B 22

0.06

0.5

<0.4

12.5

1.3

14K So

≈E410-15

E 13 1 B 22

0.06

0.5

<0.4

12.0

1.1

16/36

≈E330-15

E 18 36 Nb B 22

0.22

1.3

<0.5

18.5

35.0

2.3

17

≈E430-15

E 17 B 22

0.06

0.5

0.5

17.0

<0.6

17/06

-

EZ 17 6 B 22

<0.04

0.5

0.3

17.0

5.5

1.0

17/15 TT

-

≈E 17 13 Mn 9 W 3 B 22

0.20

10.0

0.3

17.0

14.5

<0.2

W:3.5

17/15 TTW

-

EZ 17 13 Mn 9 W 3 R 12

0.20

9.0

0.4

17.0

14.5

<0.2

W:3.5

1720

≈E430-15

E 17 Mo B 22

0.18

0.40

≤0.5

16.0

0.50

1.10

1740

-

E 17 11 B 22

0.30

0.5

0.5

16.0

0.5

1.1

18/17 E

≈E317L-15

E 18 16 5 L B 22

≤0.035

3.5

<0.4

18.0

17.5

4.5

18/17 EW

≈E317L-17

E 18 16 5 L R 32

<0.0, 35

1.2

<1,0

18.0

17.5

4.5

19/15 W

≈E316L-17

≈E 20 16 3 Mn N L R 12

≤0.04

6.0

0.6

21.0

16.5

3.0

0.18

19/15 H

≈E316L-15

E 20 16 3 Mn N L B 22

≤0.04

6.0

<0.5

20.0

16.5

3.0

0.18

20/10 W

≈E308Mo-17

E 20 10 3 R 22

0.05

1.0

0.9

20.0

10.5

3.3

20/10 W 140 K

≈E308Mo-16

E 20 10 3 R 53

0.05

0.8

0.9

20.0

10.5

3.3

20/16

-

EZ 20 16 3 Mn N L R 12

≤0.04

5.0

0.8

21.0

17.0

3.0

0.2

20/16 SM

-

EZ 22 17 4 Mn N L R 12

≤0.04

7.0

1.0

22.0

18.0

3.6

0.2

20/25 Cu

E385-15

E 20 25 5 Cu N L B 22

≤0.03

1.8

0.5

20.0

25.0

4.5

1.5

20/25 CuW

E385-16

E 20 25 5 Cu N L R 32

≤0.03

1.3

<0.7

20.0

25.0

4.5

1.5

21/33

-

≈E 21 32 Nb B 22

0.15

2.8