吸水率 (23℃.60%RH) | 0.20 | % | ASTM D-570 |
熔体流动速率 | 9 | g/10min | ASTM D-1238 |
填充材料含有率 | 25 | % | |
比重 | 1.59 | ASTM D-792 |
伸缩率 (23℃) | 3 | % | ASTM D-638 |
拉伸强度 (23℃) | 1450 | kgf/cm | ASTM D-638 |
弯曲强度 (23℃) | 2100 | kgf/cm | ASTM D-790 |
拉伸冲击强度 (3.2mmt Stype) | 180 | kgf.cm/cm | ASTM D-1822 |
曲折弹性率 (23℃) | 8.80 | ×10kgf/cm | ASTM D-790 |
断裂强度 (2mmt) | 760 | kgf/cm | ASTM D-732 |
IZOD冲击强度 (Notch 3.2mmt) | 10 | kgf.cm/cm | ASTM D-256 |
洛氏硬度 (M scale) | M95 | ASTM D-785 |
耐电压 | 23 | KV/mm | ASTM D-149 |
表面电阻率 | 1×10 | Ω | ASTM D-257 |
体积电阻率 | 1×10 | Ω.cm | ASTM D-257 |
成型收缩率 (3mmt,直径100mm) | 0.5 | % |
燃烧性 (0.8mmt) | HB | UL 94 | |
熔点 (10℃/min) | 165 | ºC | DSC Method |
线膨胀系数 (20ºC-80ºC) | 2-3 | ×10-5cm/cm/°C | ASTM D-696 |
热变形温度 | ASTM D-648 | ||
(18.6kgf/cm) | 163 | ºC | |
(4.6kgf/cm) | 164 | ºC |