熔体流动速率 | 9 | g/10min | ASTM D-1238 |
吸收率 (23℃ 60%RH) | 0.22 | % | ASTM D-570 |
比重 | 1.44 | ASTM D-792 | |
伸长率 (23℃) | 30 | % | ASTM D-638 |
成型收缩率 (t3mm 直径100mm) | 2.0 | % |
弯曲强度 (23℃) | 880 | kgf/cm | ASTM D-790 |
拉伸强度 (23℃) | 630 | kgf/cm | ASTM D-638 |
弯曲弹性率 (23℃) | 2.70×104 | kgf/cm | ASTM D-790 |
拉伸冲击强度 (t3.2mm Stype) | 90 | kgf.cm/cm | ASTM D-1822 |
IZOD缺口冲击强度 (Notch t3.2mm) | 5.5 | kgf.cm/cm | ASTM D-256 |
洛氏硬度 | 80 | M | ASTM D-785 |
表面电阻率 | 1×1016 | Ω | ASTM D-257 |
体积电阻率 | 1×1014 | Ω.cm | ASTM D-257 |
阻燃性 (t0.8mm) | HB | UL-94 | |
线性膨胀系数 (20℃ -80℃) | 13×10-5 | mm/mm/℃ | ASTM D-696 |
熔点 (10℃/min) | 165 | ℃ | DSC Method |
热变形温度 | ASTM D-648 | ||
(18.6kgf/cm) | 110 | ℃ | |
(4.6kgf/cm) | 158 | ℃ |