产品简介
详细说明
| 比重 | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| 熔体质量流动速率 | 13 | g/10 min | ASTM D792, ISO 1183 |
| 成型收缩率 | |||
| (flow,3.00MM) | 2.0 | % | ASTM D955 |
| (3.00mm) | 2.0 | % | ISO 294-4 |
| 吸水率 (E,23℃,60%rh) | 0.22 | % | ASTM D570 |
| 洛氏硬度 (M-Scale) | 82 | ASTM D785 |
| 拉伸强度 | |||
| (Yield,23℃) | 65.0 | MPa | ASTM D638 |
| (Yield,23℃) | 70.0 | MPa | ISO 527-2 |
| 拉伸伸长率 | |||
| (Break,23℃) | 55 | % | ASTM D638 |
| (Break,23℃) | 30 | % | ISO 527-2 |
| 弯曲模量 | |||
| (23°C) | 2790 | MPa | ASTM D790 |
| (23°C) | 2800 | MPa | ISO 178 |
| 弯曲强度 | |||
| (23°C) | 93.0 | MPa | ASTM D790 |
| (23°C) | 94.0 | MPa | ISO 178 |
| 剪切强度 (2.00mm) | 56.0 | MPa | ASTM D732 |
| 夏比缺口冲击强度 | 7.5 | kJ/m² | ISO 179/1eA |
| IZOD缺口冲击强度 (3.20mm) | 69.0 | J/m | ASTM D256 |
| 表面电阻率 | |||
| 1.0E+16 | ohms | ASTM D257 | |
| 1.0E+14 | ohms | IEC 60093 | |
| 体积电阻率 | |||
| 1.0E+14 | ohm·cm | ASTM D257 | |
| 1.0E+12 | ohm·cm | IEC 60093 | |
| 电气强度 | 19 | kV/mm | ASTM D149, IEC 60243-1 |
| 介电常数 (1E+6 Hz) | 3.70 | ASTM D150 | |
| 介质损耗因数 (1E+6 Hz) | 0.0070 | ASTM D150 |
| 热畸变温度 | ASTM D648 | ||
| (0.45MPa,未退火) | 158 | °C | |
| (1.8MPa,未退火) | 112 | °C | |
| (1.8MPa,未退火) | 110 | °C | |
| 熔融温度 | 165 | °C | DSC |
| 线性热膨胀系数 (flow,20 to 80°C) | 0.00013 | cm/cm/°C | ASTM D696 |
| 阻燃等级 (0.8mm) | HB | UL 94 |
在线询盘/留言
免责声明：以上所展示的信息由企业自行提供，内容的真实性、准确性和合法性由发布企业负责，本网对此不承担任何保证责任。我们原则 上建议您选择本网高级会员或VIP会员。
企业信息
最新供应
- Jws1505新能源碳中和紧迫局势
- LEADER 5851V 科技是生产力的源泉
- A1Sd62E库存更新全国发货
- FRN15G9S2 科技兴国解能源危机
- T019-0004 1007-0098 科技是生产力的源泉
- Kl-N20C库存更新全国发货
- HCKFS43BKS61科技兴国解能源危机
- Pase-E/E-Ew科技兴国魅力科技
- Mrj370Brj004U502 r科技兴国解能源危机
- Hc55科技兴国魅力科技
- APMSC06ADKP3科技兴国魅力科技
- Kit-H11S 科技兴国解能源危机
- Ldmr01125045W04 库存更新全国发货
- Ipc0021Rhkn Sst科技兴国解能源危机
- Ras70U科技兴国魅力科技
推荐供应