成型收缩率 (3mmt,直径100mm) | 2.0 | % | |
吸水率 (23°C,60%RH) | 0.22 | % | ASTM D-570 |
比重 | 1.41 | ASTM D-792 |
断裂强度 (2mmt) | 560 | kgf/cm | ASTM D-732 |
拉伸强度 (23℃) | 590 | kgf/cm | ASTM D-638 |
伸缩率 (23℃) | 40 | % | ASTM D-638 |
洛氏硬度 (M scale) | M80 | ASTM D-785 | |
曲折弹性率 (23°C) | 2.60 | ×10kgf/cm | ASTM D-790 |
拉伸冲击强度 (3.2mmt Stype) | 90 | kgf.cm/cm | ASTM D-1822 |
弯曲强度 (23℃) | 850 | kgf/cm | ASTM D-790 |
IZ0D冲击强度 (Notch 3.2mmt) | 5.5 | kgf.cm/cm | ASTM D-256 |
体积电阻率 | 1×10 | Ω.cm | ASTM D-257 |
表面电阻率 | 1×10 | Ω | ASTM D-257 |
导电率 (10Hz) | 3.7 | ASTM D-150 | |
个质损耗系数 (10Hz) | 0.007 | ASTM D-150 | |
耐电压 | 19 | KV/mm | ASTM D-149 |
线膨胀系数 (20°C-80°C) | 13 | ×10-5cm/cm/°C | ASTM D-696 |
熔点 (10°C/min) | 165 | °C | DSC Method |
燃烧性 (0.8mmt) | HB | UL-94 | |
热变形温度 | ASTM D-648 | ||
(18.6kgf/cm) | 110 | °C | |
(4.6kgf/cm) | 158 | °C | |
熔融指数 | 28 | g/10 min |