熔体流动速率 | |||
45 | g/10min | ASTM D1238 | |
(190℃/2.16kg) | 45 | g/10min | ISO 1133 |
吸水率 (24 hr) | 0.2 | % | ASTM D570 |
比重 | 1.41 | g/cm | ASTM D792,ISO 1183 |
成型收缩率 | |||
(Flow) | 1.6-2 | % | ASTM D955,ISO 294-4 |
(Across Flow) | 1.6-2 | % | ISO 294-4 |
洛氏硬度 | ASTM D785 | ||
(M-Scale) | 80 | ||
(R-Scale) | 115 |
拉伸模量 | 2900 | MPa | ISO 527-2 |
屈服拉伸应力 | 67 | MPa | ISO 527-2 |
拉伸应力 | 61 | MPa | ASTM D638 |
断裂伸长率 | |||
45 | % | ASTM D638 | |
30 | % | ISO 527-2 | |
弯曲模量 | 2630 | MPa | ASTM D790 |
弯曲强度 | 90 | MPa | ASTM D790 |
泰伯耐磨性 (1000 Cycles) | 14 | mg | ASTM D1044 |
CHARPY缺口冲击强度 (23℃) | 4.5 | kJ/m | ISO 179/1eA |
Izod 缺口冲强度 | 39 | J/m | ASTM D256 |
热变形温度 | |||
(0.45MPa,unannealed) | 158 | ℃ | ASTM D648 |
(0.45MPa,unannealed) | 156 | ℃ | ISO 75-2/B |
(1.8MPa,unannealed) | 110 | ℃ | ASTM D648 |
(1.8MPa,unannealed) | 105 | ℃ | ISO 75-2/A |
流动方向线性热膨胀系数 | 0.0001 | cm/cm/℃ | ASTM E831 |
阻燃等级 | HB | UL 94 |