熔体流动速率 | |||
(190℃/2.16kg) | 17 | g/10min | ISO 1133 |
17 | g/10min | ASTM D1238 | |
吸水率 (24 hr) | 0.2 | % | ASTM D570 |
比重 | 1.42 | g/cm | ASTM D792,ISO 1183 |
成型收缩率 | |||
(Flow) | 1.8-2.2 | % | ASTM D955,ISO 294-4 |
(Across Flow) | 1.8-2.2 | % | ISO 294-4 |
拉伸模量 | 3000 | MPa | ISO 527-2 |
屈服拉伸应力 | 72 | MPa | ISO 527-2 |
拉伸应力 | 68 | MPa | ASTM D638 |
断裂伸长率 | |||
50 | % | ASTM D638 | |
40 | % | ISO 527-2 | |
弯曲模量 | 2940 | MPa | ASTM D790 |
弯曲强度 | 103 | MPa | ASTM D790 |
CHARPY缺口冲击强度 (23℃) | 9 | kJ/m | ISO 179/1eA |
Izod 缺口冲强度 | 69 | J/m | ASTM D256 |
热变形温度 | |||
(0.45MPa,unannealed) | 163 | ℃ | ISO 75-2/B |
(1.8MPa,unannealed) | 96 | ℃ | ISO 75-2/A |
阻燃等级 | HB | UL 94 |