吸湿率 (湿) | 1.6 | % |
成型收缩率 (干) | 0.3/0.7 | % | 旭化成方法 |
比重 (干) | 1.50 | ASTM D-792 |
拉伸强度 (干(湿)) | 186(132) | MPa | ASTM D-638 |
抗挠强度 (干(湿)) | 304(177) | MPa | ASTM D-790 |
洛氏硬度 (干(湿)) | 118(-) | R scale | ASTM D-785 |
抗挠系数 (干(湿)) | 11.0(5.9) | GPa | ASTM D-790 |
悬臂梁式缺口冲击强度 (干(湿)) | 147(226) | J/M | ASTM D-256 |
洛氏硬度 (干(湿)) | 93(-) | M scale | ASTM D-785 |
断裂延伸率 (干(湿)) | 3(4) | % | ASTM D-638 |
热变形温度 | ASTM D-648 | ||
(0.46MPa,干) | 250 | ℃ | |
(1.82MPa,干) | 240 | ℃ | |
阻燃性 (干) | HB |