吸湿率 (湿) | 2.2 | % |
比重 (干) | 1.14 | ASTM D-792 | |
磨耗率 (湿) | 6 | ×10-6kg/1000times | ASTM D-1044 |
成型收缩率 (干) | 0.9-1.6 | % | 旭化成方法 |
断裂延伸率 (干(湿)) | 35(200) | % | ASTM D-638 |
拉伸强度 (干(湿)) | 88(67) | MPa | ASTM D-638 |
抗挠系数 (干(湿)) | 3.0(1.3) | GPa | ASTM D-790 |
悬臂梁式缺口冲击强度 (干(湿)) | 39(108) | J/M | ASTM D-256 |
抗挠强度 (干(湿)) | 128(59) | MPa | ASTM D-790 |
洛氏硬度 | ASTM D-785 | ||
(干(湿)) | 120(110) | R scale | |
(干(湿)) | 85(60) | M scale |
阻燃性 (干) | V-2 | UL 94 | |
导热率 (干) | 0.2 | W/(m.k) | |
线性膨胀系数 (干) | 8 | ×10-5/K | ASTM D-696 |
热变形温度 | ASTM D-648 | ||
(0.46MPa,干) | 240 | ℃ | |
(1.82MPa,干) | 75 | ℃ | |
比热容 (干) | 1670 | J/(kg.k) |
氧指数 (干) | 26 | % | ASTM D-2863 |