吸湿率 (湿) | 0.9 | % |
比重 (干) | 1.52 | ASTM D-792 | |
成型收缩率 (干) | 0.4-0.9 | % | 旭化成方法 |
磨耗率 (湿) | 24 | ×10-6kg/1000times | ASTM D-1044 |
拉伸强度 (干(湿)) | 153(123) | MPa | ASTM D-638 |
洛氏硬度 (干(湿)) | 95(55) | M scale | ASTM D-785 |
悬臂梁式缺口冲击强度 (干(湿)) | 63(72) | J/M | ASTM D-256 |
断裂延伸率 (干(湿)) | 2.5(2.7) | % | ASTM D-638 |
抗挠系数 (干(湿)) | 7.6(5.9) | GPa | ASTM D-790 |
抗挠强度 (干(湿)) | 216(177) | MPa | ASTM D-790 |
热变形温度 (1.82MPa,干) | 248 | ℃ | ASTM D-648 |
阻燃性 (干) | V-0 | UL 94 | |
热变形温度 (0.46MPa,干) | 255 | ℃ | ASTM D-648 |
线性膨胀系数 (干) | 3 | ×10-5/K | ASTM D-696 |
氧指数 (干) | 37 | % | ASTM D-2863 |