吸湿率 (湿) | 2.5 | % |
比重 (干) | 1.14 | ASTM D-792 | |
磨耗率 (湿) | 4 | ×10-6kg/1000times | ASTM D-1044 |
成型收缩率 (干) | 1.3-2.0 | % | 旭化成方法 |
抗挠强度 (干(湿)) | 118(54) | MPa | ASTM D-790 |
洛氏硬度 | ASTM D-785 | ||
(干(湿)) | 120(105) | R scale | |
(干(湿)) | 80(55) | M scale | |
悬臂梁式缺口冲击强度 (干(湿)) | 49(245) | J/M | ASTM D-256 |
抗挠系数 (干(湿)) | 2.8(1.2) | GPa | ASTM D-790 |
拉伸强度 (干(湿)) | 80(59) | MPa | ASTM D-638 |
断裂延伸率 (干(湿)) | 100(300) | % | ASTM D-638 |
热变形温度 (1.82MPa,干) | 70 | ℃ | ASTM D-648 |
比热容 (干) | 1670 | J/(kg.k) | |
导热率 (干) | 0.2 | W/(m.k) | |
线性膨胀系数 (干) | 8 | ×10-5/K | ASTM D-696 |
热变形温度 (0.46MPa,干) | 230 | ℃ | ASTM D-648 |
氧指数 (干) | 23 | % | ASTM D-2863 |