比重 | 1.16 | g/cm³ | ASTM D792 |
熔流率 (190℃/2.16 kg) | 7.0 | g/10 min | ASTM D1238 |
收缩率 (流动) | 0.80 | % | ASTM D955 |
吸水率 (24hr) | 0.60 | % | ASTM D570 |
硬度计硬度 (邵氏 D) | 40 | ASTM D2240 |
抗张强度 (断裂) | 26.5 | MPa | ASTM D638 |
(5.0% 应变) | 2.35 | MPa | ASTM D638 |
(10% 应变) | 4.31 | MPa | ASTM D638 |
伸长率 (断裂) | 680 | ASTM D638 | |
弯曲模量 | 66.7 | MPa | ASTM D790 |
悬臂梁缺口冲击强度 | 无断裂 | ASTM D256 |
熔融温度 | 155 | ℃ |