物理性能额定值单位测试方法比重1.17g/cm³ASTM D792
1.15g/cm³ISO 1183熔流率 (190℃/2.16 kg)5.3g/10 minASTM D1238(190℃/2.16kg)5.6g/10 minISO 1133溶化体积流率 (190℃/2.16 kg)5.00cm³/10minISO 1133收缩率(流动)0.50%ASTM D955



(横向流量: 2.00 mm)0.50%ISO294-4(流量: 2.00 mm)0.50%ISO 294-4吸水率 (23℃,24 hr)0.60%ASTM D570, ISO 62



(饱和, 23℃)0.70%ISO62(平衡, 23℃, 50% RH)0.20%ISO 62硬度 (支撐D)40
ASTM D2240, ISO 868(支撐 D.15秒)39
ISO 868机械性能额定值单位测试方法拉伸模量 (23℃)53.0MPaISO 527-2抗张强度 ( 断裂,23℃)21.0MPaASTM D638



( 断裂, 23℃)30.0MPaISO527-2(5.0%应变, 23℃)2.40MPaASTMD638( 10%应变, 23℃)3.60MPaASTMD638( 50%应变, 23℃)7.50MPaISO 527-2伸长率 (断裂,23℃)700%ASTM D638(断裂, 23℃)420%ISO 527-2断张率 (23℃)570%ISO 527-2拉伸蠕变模量(1 hr)54.0MPaISO 899-1(1000 hr)40.0MPaISO 899-1弯曲模量(-40℃)155MPaASTM D790, ISO 178



(23℃)62.0MPaASTM D790, ISO178(100℃)27.0MPaASTM D790, ISO 178TensileStress ( 23℃, 10% Strain )4.20MPaISO 527-2( 23℃, 5% Strain)2.40MPaISO 527-2简支梁缺口冲击强度 (-40℃)70kJ/m²ISO 179/1eA



(-30℃)无断裂
ISO 179/1eA(23℃)无断裂
ISO 179/1eA简支梁缺口冲击强度 (-30℃)无断裂
ISO 179/1eU(23℃)无断裂
ISO 179/1eU悬壁梁缺口冲击强度 (-40℃)无断裂
ASTM D256, ISO 180/1A(23℃)无断裂
ASTM D256, ISO 180/1A拉伸冲击强度 (23℃)230kJ/m²ISO 8256热性能额定值单位测试方法热变形温度(0.45 MPa, 未退火)54.0℃ASTM D648(0.45 MPa, 未退火)50.0℃ISO 75-2/B脆化温度<-100℃ISO 974玻璃转化温度-50.0℃ISO 11357-2熔融温度150℃ISO 11357-3, ASTMD3418线形膨胀系数 (流动: -40 到 23℃)0.00020cm/cm/℃ASTM E831, ISO 11359-2



(流动: 23 到 55℃)0.00013cm/cm/℃ASTM E831, ISO11359-2(流动: 55 到 85℃)0.00010cm/cm/℃ASTME831, ISO 11359-2(横向: -40 到23℃)0.00018cm/cm/℃ASTM E831, ISO11359-2(横向: 23 到 55℃)0.00016cm/cm/℃ASTME831, ISO 11359-2(横向: 55 到85℃)0.00016cm/cm/℃ASTM E831, ISO11359-2电气性能额定值单位测试方法表面电阻率2.0E+14ohmsIEC 60093体积电阻率7.0E+12ohm·cmIEC60093介电强度 (23℃, 1.91 mm3)16kV/mmASTM D149(23℃)18kV/mmIEC60243-1介电常数 ( 23℃, 1.91 mm, 100 Hz )5.2
ASTM D150



( 23℃, 1.91 mm, 1 kHz )5.10
ASTM D150( 23℃, 1.91 mm, 1 MHz )4.60
ASTM D150( 23℃, 100 Hz )5.20
IEC 60250( 23℃, 1 Hz )4.70
IEC 60250耗散因数 ( 23℃, 1.91 mm, 100 Hz )0.0050
ASTM D150



( 23℃, 1.91 mm, 1Hz )0.0080
ASTM D150( 23℃, 1.91 mm, 1Hz )0.060
ASTM D150( 23℃, 100 Hz )0.011
IEC 60250( 23℃, 1 Hz )0.053
IEC 60250漏电起痕指数> 600VIEC 60112UL 阻燃等级 (1.50 mm)HB
UL 94可燃性等级 (1.50 mm)HB
IEC 60695-11-10, -20极限氧指数20%ISO 4589-2RTI Str (1.50 mm)50.0℃UL746RTI Imp (1.50 mm)50.0℃UL 746RTI Elec (1.50 mm)50.0℃UL 746